General Characteristics: Thermoplastics Grades
CHARACTERISTICS | CONDITIONS | STANDARD | UNITS | 7233 | 7033 | 6333 | 5533 | 4033 | 4533 | 3533 | 2533 | ||||||||
SHORE HARDNESS |
instantaneous | ISO 868/ ASTM D 2240 | Shore D | 69 | 69 | 64 | 54 | 42 | 46 | 33 | 27 | ||||||||
Shore A | - | - | - | - | 90 | 92 | 82 | 77 | |||||||||||
after 15 seconds | ISO 868/ ASTM D 2240 | Shore D | 61 | 61 | 58 | 50 | 35 | 41 | 25 | 22 | |||||||||
Shore A | - | - | - | - | 89 | 90 | 80 | 74 | |||||||||||
DENSITY | ISO 1183 | g/cm3 | 1.01 | 1.01 | 1.01 | 1.01 | 1.00 | 1.01 | 1.00 | 1.00 | |||||||||
MELTING POINT |
ISO 11357/ ASTM D 3418 | °C | 174 | 172 | 169 | 159 | 160 | 147 | 143.5 | 133.5 | |||||||||
VICAT SOFTENING POINT |
under 10 N | ISO 306/ ASTM D 1525 | °C | 164 | 164 | 157 | 142 | 131 | 111 | 77 | 58 | ||||||||
WATER ABSORPTION AT EQUILIBRIUM |
at 23°C and 50% RH | ISO 62/ ASTM D 570 | % | 0.7 | 0.7 | 0.7 | 0.6 | 0.5 | 0.4 | 0.4 | 0.4 | ||||||||
WATER ABSORPTION SATURATION |
24h in water at 23°C | ISO 62/ ASTM D 570 | % | 0.9 | 0.9 | 1.1 | 1.2 | 1.2 | 1.2 | 1.2 | 1.2 | ||||||||
MELT INDEX | 235°C / 1kg | ISO 1133/ ASTM D 1238 | g/10 mn | 4 | 6 | 5 | 7 | 5 | 9 | 8 | 10 | ||||||||
LINEAR COEFFICIENT OF THERMAL EXPANSION |
from - 40°C to +140°C | ASTM D 696 | 10-5/°C | 12 | 16 | 14 | 17 | 19.5 | 20 | 21 | 20 | ||||||||
SURFACE RESISTIVITY |
IEC 60093/ ASTM D 257 | Ohm/sq | ›1012 | ||||||||||||||||
VOLUMIC RESISTIVITY |
Ohm.cm | ||||||||||||||||||
FILLER | - | - | - | - | - | - | - | - |
Properties (Plastic Materials Tests)
CHARACTERISTICS | CONDITIONS | STANDARD | UNITS | 7233 | 7033 | 6333 | 5533 | 4033 | 4533 | 3533 | 2533 | ||||||||
FLEXURAL MODULUS | ISO 178 | MPa | 513 | 390 | 285 | 170 | 77 | 86 | 21 | 12 | |||||||||
ASTM D 790 | MPa | 518 | 379 | 278 | 164 | 81 | 93 | 20 | 14 | ||||||||||
TENSILE MODULUS | ISO 527 | MPa | 522 | 384 | 280 | 161 | 71 | 81 | 18 | 10 | |||||||||
ASTM D 638 | MPa | 521 | 383 | 287 | 160 | 74 | 79 | 20 | 10 | ||||||||||
TENSILE – STRESS AT YIELD | v = 50 mm/min | ASTM D 638 type IV | MPa | 26 | 22 | 18 | 12 | - | - | - | - | ||||||||
TENSILE – STRAIN AT YIELD | % | 18 | 20 | 22 | 25 | - | - | - | - | ||||||||||
TENSILE – STRESS AT BREAK | MPa | 56 | 54 | 53 | 52 | 40 | 42 | 39 | 32 | ||||||||||
TENSILE – STRAIN AT BREAK | % | ›300 | ›350 | ›350 | ›450 | ›450 | ›550 | ›600 | ›750 | ||||||||||
IMPACT STRENGTH * (IZOD) AT + 23 °C | unnotched | ASTM D 256 | J/m | 1380 p | 969 p | 607 p | N | N | N | N | N | ||||||||
notched | 192 c | 847 p | 554 p | N | N | N | N | N | |||||||||||
IMPACT STRENGTH * (IZOD) AT - 40 °C | unnotched notched |
ASTM D 256 | J/m | 2460 p | 2345 p | 1589 p | 1589 p | N | N | N | N | ||||||||
50 c | 50 c | 11 c | 1038 p | N | N | N | N | ||||||||||||
IMPACT STRENGTH * (CHARPY) AT + 23 °C | unnotched | ISO 179 | kJ/m2 | N | N | N | N | N | N | N | N | ||||||||
notched | 15 c | 120 p | N | N | N | N | N | N | |||||||||||
IMPACT STRENGTH * (CHARPY) AT - 30 °C | unnotched | ISO 179 | kJ/m2 | N | N | N | N | N | N | N | N | ||||||||
notched | 10 c | 10 c | 20 c | N | N | N | N | N |